TEKNOZINC 90 SE
Zinc rich epoxy paint
- Corrosion protective
- 2-component
- Primer
- Corrosion protective
- 2-component
- Primer
TEKNOZINC 90 SE is a two-pack solvent-borne zinc rich epoxy paint.
Used as a primer in polyurethane and epoxy coating systems. Protects steel efficiently from underfilm corrosion and resists weathering even without any top coat. The paint comes up to the specifications of both standard EN-ISO 12944-5 and the Swedish reference book 'Boverkets handbok om stålkonstruktioner' (BSK07). The zinc content of the paint is at least 90% by weight in the dry paint film. The paint comes up to the specifications of Swedish Standard SSG 1022-GB. TEKNOZINC SE WINTER HARDENER is to be used when painting at temperatures below +10°C.
Surface preparation
Remove from the surfaces any contaminants that might be detrimental to surface preparation and application. Remove also water-soluble salts by using appropriate methods. The surfaces are prepared according to the different materials as follows:
STEEL SURFACES: Remove mill scale and rust by blast cleaning to preparation grade Sa 2½ (standard ISO 8501-1).
OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities that might be detrimental to the application of paint (e.g. grease and salts) are removed. The surfaces must be dry and clean. Old, painted surfaces that have exceeded the maximum overcoating time are to be roughened as well. Damaged parts are prepared in accordance with the requirements of the substrate and the maintenance coating.
The place and time of the preparation are to be chosen so that the prepared surface will not get dirty or damp before the subsequent treatment.
Additional instructive information for surface preparation can be found in standards EN ISO 12944-4 and ISO 8501-2.
Prefabrication primer: KORRO SE Zinc Epoxy and KORRO SS Zinc Silicate Prefabrication Primers can be used, when required.
Application
MIXING OF THE COMPONENTS: Take into consideration the pot life of the mixture when estimating the amount to be mixed at a time. Before application the base and hardener are mixed in right proportion. Stir thoroughly down to the bottom of the vessel. Inadequate stirring or incorrect mixing ratio results in imperfect curing and impaired film properties.
Stir the paint frequently in the course of work, about every half an hour, in order to prevent sedimentation of the zinc dust.
Application conditions
The surface to be treated must be dry. During the application and drying period the temperature of the ambient air, the surface and the product shall be above +10°C and the relative air humidity below 80%. Additionally, the temperature of the surface to be treated and the product must be at least +3°C above the dew point of the ambient air.
When using TEKNOZINC SE WINTER HARDENER the temperature of the ambient air and the surface to be painted shall be over -5°C. The temperature of the paint during the mixing and application is to be above +15°C. The surface to be treated must be free from ice.
Storage
The storage stability is shown on the label. Store in a cool place and in tightly closed containers.
Suitable airless nozzle size (turn-nozzle) 0.018 - 0.021".
| Total mass of solids | abt. 2100 g/l |
|---|---|
| Volatile organic compound (VOC) | abt. 450 g/l |
| Pot life | 16 h (+23 °C) |
| Mixing ratio | 5:1 by volume (comp. A : comp. B) |
| Hardener | Comp. B: TEKNOZINC 50 SE / 80 SE / 90 SE HARDENER |
| Gloss | Matt |
| Practical spreading rate | The values depend on the application technique, surface conditions, overspray, etc. |
| Drying time – dust free | 5 min (ISO 9117-3:2010) |
| Drying time – touch dry | 30 min (ISO 9117-5:2012) |
| Drying time – fully cured | 7 d |
| Thinner | TEKNOSOLV 9506 |
| Clean up | TEKNOSOLV 9506 |
| Colours | Bluish grey. |
| Safety markings | See safety data sheet. |
| Approvals & certificates | Boverkets handbok om stålkonstruktioner (BSK07),EN ISO 12944-5,SSG 1022-GB |