TEKNODUR STRUCTURE 3615
Polyurethane top coat
- Corrosion protective
- 2-component
- Solvent-borne
- Single coat paint
- Topcoat
TEKNODUR STRUCTURE 3615 semi gloss and structured two pack polyurethane paint with an aliphatic polyisocyanate as a hardener.
The paint can be used as a topcoat in polyurethane coating systems in combination with a primer. With an appropriate surface preparation (SA2½, FePho, ZnPho) it can also be used as one layer coating system.
Low solvent content. Quick drying. Excellent adhesion on smooth and blasted steel substrates. When used as one layer coating an effective corrosion protection can be achieved. Structured surface easy achievable by using common applications techniques.
Surface preparation
Remove from the surface any contaminants that might be detrimental to surface
preparation and coating. Remove also water-soluble salts by using appropriate
methods. The surface should be prepared as follows:
STEEL SURFACES: Remove mill scale and rust by blast cleaning to preparation
grade Sa 2½ (standard ISO 8501-1). Roughening the surface of thin-plate
improves the adhesion of the paint to the substrate.
ZINC SURFACES: Hot-dip-galvanized steel structures that are exposed to
atmospheric corrosion can be painted if the surfaces are sweep blast-cleaned
(SaS) till matt all over. Suitable cleaning agents are, e.g. aluminium oxide and
natural sand. It is not recommended to paint galvanized objects that are
subjected to immersion strain.
It is recommended that new zinc-coated thin-plate structures are treated with
sweep blast-cleaning (SaS). Surfaces that have been weathered to matt can be
treated also with PELTIPESU Cleaning Agent.
OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities
that might be detrimental to the application of paint (e.g. grease and salts) are to
be removed. The surface must be dry and clean. Old, painted surfaces that have
exceeded the maximum overcoating time are to be roughened as well. Damaged
parts are prepared in accordance with the requirements of the substrate and the
maintenance coating.
| Solids | abt. 52 % by volume |
|---|---|
| Total mass of solids | abt. 1050 g/l |
| Weight solids | abt. 70 % by weight |
| Volatile organic compound (VOC) | abt. 440 g/l |
| Pot life | 4 h (+23 °C) |
| Mixing ratio | 6,5:1 by volume (comp. A : comp. B) |
| Hardener | Comp. B: TEKNODUR HARDENER 7255 |
| Gloss | Semi-gloss |
| Tinting system | Teknotint |
| Drying time – dust free | after 30 min |
| Drying time – touch dry | after 1.5 h |
| Drying time - overcoatable | After min. 3 h / max. 1 month |
| Thinner | TEKNOSOLV 6740 |
| Clean up | TEKNOSOLV 6740 |