TEKNODUR 9201-05
2C-polyurethane topcoat
- Corrosion protective
- Special adhesion
- 2-component
- Solvent-borne
- Topcoat
TEKNODUR 9201-05 is a high-quality, versatile polyurethane topcoat. The hardener is an aliphatic isocyanate resin.
TEKNODUR 9201-05 is a semi-gloss, two-component topcoat for smooth and blasted steel surfaces. It is characterized by excellent corrosion resistance, high-quality finish, good weather resistance and a very good adhesion on steel surfaces.
Surface preparation
Remove from the surfaces any contaminants that might be detrimental to surface preparation and application. Remove also water-soluble salts by using appropriate methods. The surfaces are prepared according to the different materials as follows:
STEEL SURFACES: Remove mill scale and rust by blast cleaning to preparation grade Sa 2½ (standard ISO 8501-1). Roughening the surface of thin-plate improves the adhesion of the paint to the substrate.
OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities that might be detrimental to the application of paint (e.g. grease and salts) are removed. The surfaces must be dry and clean. Old, painted surfaces that have exceeded the maximum overcoating time are to be roughened as well.
The place and time of the preparation are to be chosen so that the prepared surface will not get dirty or damp before the subsequent treatment.
Additional instructive information for surface preparation can be found in standards EN ISO 12944-4 and ISO 8501-2.
Application
Take into consideration the pot life of the mixture when estimating the amount to be mixed at a time. Before application the base and hardener are mixed in right proportion. Stir thoroughly down to the bottom of the vessel. Inadequate stirring or incorrect mixing ratio results in imperfect curing and impaired film properties.
Stir thoroughly before use.
Application conditions
The surface to be treated must be dry. During the application and drying period the temperature of the ambient air, the surface and the product shall be above +5°C and the relative air humidity below 80%. Additionally, the temperature of the surface to be treated and the product must be at least +3°C above the dew point of the ambient air. During application good ventilation is recommended.
Storage
The storage stability is shown on the label. Store in a cool place and in tightly closed containers. The hardener reacts with air humidity and therefore the opened can is to be kept carefully closed, and it is recommended to be used within 14 d of opening.
| Solids | abt. 43 % by volume |
|---|---|
| Weight solids | abt. 57 % by weight |
| Volatile organic compound (VOC) | abt. 493 g/l |
| Pot life | 4 h (+23 °C) |
| Mixing ratio | 7:1 by volume (comp. A : comp. B) |
| Hardener | Comp. B: TEKNODUR HARDENER 7255 or TEKNODUR HARDENER 7236 |
| Gloss | Semi-gloss |
| Density | abt. 1.16 g/ml |
| Practical spreading rate | The values depend on the application technique, surface conditions, overspray, etc. |
| Drying time – dust free | 30 min |
| Drying time – touch dry | 4 h |
| Drying time – forced drying | 30 min at 60°C |
| Thinner | TEKNOSOLV 6740 |
| Clean up | TEKNOSOLV 6740 |
| Colours | RAL 2008 |
| Safety markings | See safety data sheet. The hardener of the product and the ready mixture contain isocyanates. In poorly ventilated areas and especially when using spray application we recommend the use of a fresh air mask. In short or temporary work, a mask with combined filter A2-P2 can be used. In this case eyes and face are to be protected. The hardener can must be opened with caution, as pressure may develop in the can during storage. |