TEKNODUR 9204-20L
Polyurethan top coat
- Electrical insulation
- Heat resistant
- 2-component
- Solvent-borne
- Single coat paint
- Topcoat
TEKNODUR 9204-20L is a matt two-pack high-solid polyurethane paint with an aliphatic polyisocyanate as a hardener.
With an appropriate surface preparation (SA2½, FePho, ZnPho) it can also be used as one layer coating system.
Low solvent content. Quick drying. Good mechanical and weather resistance. Excellent adhesion on different types of substrate. Temperature resistance: +120°C continuous (dry heat), +150°C short-term Conductive setting. Meets ATEX criteria for electronic assemblies (Electric motors, etc.).
Technical data sheet
Surface preparation
Remove from the surface any contaminants that might be detrimental to surface
preparation and coating. Remove also water-soluble salts by using appropriate
methods. The surface should be prepared as follows:
STEEL SURFACES: Remove mill scale and rust by blast cleaning to preparation
grade Sa 2½ (standard ISO 8501-1). Roughening the surface of thin-plate
improves the adhesion of the paint to the substrate.
ZINC SURFACES: Hot-dip-galvanized steel structures that are exposed to
atmospheric corrosion can be painted if the surfaces are sweep blast-cleaned
(SaS) till matt all over. Suitable cleaning agents are, e.g. aluminium oxide and
natural sand. It is not recommended to paint galvanized objects that are
subjected to immersion strain.
It is recommended that new zinc-coated thin-plate structures are treated with
sweep blast-cleaning (SaS). Surfaces that have been weathered to matt can be
treated also with PELTIPESU Cleaning Agent.
The place and the time of the preparation are to be chosen so that the prepared
surface will not get dirty or damp before subsequent treatment.
OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities
that might be detrimental to the application of paint (e.g. grease and salts) are to
be removed. The surface must be dry and clean. Old, painted surfaces that have
exceeded the maximum overcoating time are to be roughend as well. Damaged
parts are prepared in accordance with the requirements of the substrate and the
maintenance coating.
| Solids | abt. 58 % by volume |
|---|---|
| Weight solids | abt. 75 % by weight |
| Volatile organic compound (VOC) | abt. 370 g/l |
| Pot life | 3 h (+23 °C) |
| Mixing ratio | 9:1 by volume (comp. A : comp. B) |
| Hardener | Comp. B: TEKNODUR HARDENER 7500 |
| Gloss | Matt |
| Drying time – dust free | after 30 min |
| Drying time – touch dry | after 2 h |
| Drying time – forced drying | 60°C / 1 h (grasp) |
| Drying time - overcoatable | after 1 h |
| Thinner | TEKNOSOLV 6740 |
| Clean up | TEKNOSOLV 6740 |