TEKNODUR AQUA 3390-09

Remove from the surfaces any contaminants that might be detrimental to surface preparation and application. Remove also water-soluble salts by using appropriate methods. The surfaces are prepared according to the different materials as follows: OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities that might be detrimental to the application of paint (e.g. grease and salts) are removed. The surfaces must be dry and clean. Old, painted surfaces that have exceeded the maximum overcoating time are to be roughened as well. Damaged parts are prepared in accordance with the requirements of the substrate and the maintenance coating. The place and time of the preparation are to be chosen so that the prepared surface will not get dirty or damp before the subsequent treatment. Additional instructive information for surface preparation can be found in standards EN ISO 12944-4 and ISO 8501-2.

The base and hardener are mixed together and stirred mechanically thoroughly before application down to the bottom of the vessel. The hardener is mixed undivided and in one go into the base. The stirring time is at least 5 min. Inadequate stirring or incorrect mixing ratio results in imperfect curing and impaired film properties. Ready paint is to be used within 1½ h from mixing. After this the mixture is unfit for use. For the application it is recommended to use airless spray (nozzle 0.011-0.013") or conventional spray. Conventional spray gives the best result. The components are not to be thinned separately. Once the hardener is added, do not seal the vessel as small amounts of carbon dioxide produced in the paint may cause pressure build up.

The surface to be treated must be dry. During the application and drying period the temperature of the ambient air, the surface and the product shall be above +10 °C and the relative air humidity below 70%. Additionally, the temperature of the surface to be treated and the product must be at least +3°C above the dew point of the ambient air. Especially when applying with a spray the relative air humidity should be above 30% to avoid the onset of the drying process to be too fast. Surface temperature, film thickness, drying temperature and ventilation affect the drying of the paint. The paint is dry when all water has evaporated from the paint film. It is essential that all painted surfaces have sufficient ventilation. If the painted surface will be exposed to weathering, moisture or low temperatures (below +10°C) thick paint films are to be avoided and the last coat must be allowed to dry for at least 24 hours (at +23°C) before exposure. Low temperatures and insufficient ventilation slow down the drying process.

The storage stability is shown on the label. Store indoors in a cool and dry place and in a tightly closed can. The hardener reacts with air humidity and therefore the opened can is to be kept carefully closed, and it is recommended to be used within 14 d of opening.