INFRALIT PE 8340-00

Polyester powder

»
  • Powder coating

INFRALIT PE 8340-00 is a TGIC-free powder coating based on solid high quality polyester resin. At elevated temperature the powder will melt, cure and form the final paint film.

INFRALIT PE 8340-00 is suitable for steel and aluminium constructions in objects where good weather resistance is required. INFRALIT PE 8340-00 forms a mechanically and chemically resistant paint film which has good corrosion resistance and very good colour stability and gloss retention also in outdoor conditions.

Surface preparation

STEEL SURFACES: Remove grease and dirt. After that blast-cleaning at least to preparation grade Sa 2½ (ISO 8501-1) and/or a suitable chemical pretreatment. ALUMINIUM SURFACES: Remove grease and dirt. After that chromating or alternatively a suitable chemical pretreatment. HOT-DIP-GALVANIZED AND ZINC-ELECTROPLATED SURFACES: Remove grease, dirt and white rust by e.g. alkali wash. Depending on exposure conditions, chromating or alternatively a suitable chemical pretreatment is also required.

Storage

The storage life is minimum 18 months in dry and cool conditions when the temperature during storage and transportation is max. +25°C. Take special care during high temperature seasons. Avoid storing close to heat sources and heaters in trucks and storages. Don’t store in direct sunlight. The recommended expiry date of the powder coating that has been stored according to the instructions is shown on the package label.
Practical spreading rate 6 - 10 m²/kg depending on the film thickness.
Spraying TRIBO/CORONA
Curing time 10 min/180°C (metal temperature)
Colours By agreement.
Packages 15 kg or 20 kg according to the density of the powder.
Safety markings See safety data sheet. The powder itself is non-flammable, but with air it can form an explosive mixture that in presence of adequate ignition energy ignites. The lower explosion limit of typical powder coatings is between 20 g/m³ and 80 g/m³ (CEPE, Safe Powder Coating Guideline 8th Edition, 2020). Ventilation of the spray booth should be adjusted so that the concentration of powder in the air is less than 50% of the lower explosive limit value. On calculation of the powder concentration in the spray booth, the powder deposited on the workpiece is not taken into account. In order to avoid the discharge of powder from the booth into adjacent working spaces, the speed of air flow in the apertures of the booth must not fall below 0.5 m/s. Spray painters should wear dust masks and protective gloves. Any spatter of powder on the skin should be washed off with water and soap.
Gloss value 50-65