EPIRUST ALU-STEEL PRIMER 2002

Epoxy primer

  • Corrosion protective
  • Water resistant
  • 2-component
  • Primer
  • Solvent-borne

Two components, modified epoxy primer, fast curing with amine adduct.

Priming the hulls and equipment parts from steel, aluminum and cast iron.

Can be applied on wet and not well cleaned surfaces, humidity insensitive. The coating cures very fast even in low temperatures and is not sensitive to water (rain) when cured to touch dry degree.. High reactive coating with long pot life. Flexible coating, with good adhesion to surfaces and resistant to mechanical factors. The coating resistant to weathering, water, salt and alkali solutions, oil, fuel oil, diesel, motor gasoline and some organic solvents. Coating resistant to the elements occurring in the cathodic protection.

Surface preparation

It is recommended to wash surface with water with addition of OLIVA CLEANER and then rinse with fresh water.

Application

Airless spray, brush. When using a brush it may be necessary to apply several layers to achieve recommended coating thickness. Airless spray parameter - nozzle size: 0,38 - 0,48 mm, nozzle pressure: 15 – 20 MPa.

Application conditions

Minimum surface temperature: -5°C (surface frost- and ice-free), minimum temperature of paint itself +15°C, ambient temperature not lower than -10°C, relative air humidity below 95%, good ventilation.
Solids abt. 51 % by volume
Volatile organic compound (VOC) abt. 380 g/l
Pot life 8 h (+23 °C)
Mixing ratio 100:22 by volume (comp. A : comp. B)
Hardener Comp. B: UTWARDZACZ 161
Recommended film thickness Dry film (µm) 40. Wet film (µm) 80.
Drying time – dust free after 25 min.
Drying time – touch dry after 50 min.
Thinner Not recommended. When necessary (for example – thickening product) use TEKNOSOLV 564.
Clean up TEKNOSOLV 564
Packages Base: 0,6 l Hardener: 0,14 l
Safety markings See Safety Data Sheet