TEKNONISO COMBI 333-300

Remove from the surfaces any contaminants that might be detrimental to surface preparation and application. Remove also water-soluble salts by using appropriate methods. The surfaces are prepared according to the different materials as follows: STEEL SURFACES: Remove mill scale and rust by blast cleaning to preparation grade Sa 2½ (standard ISO 8501-1). The profile of the blast-cleaned surface should be coarse (reference comparator "G") ISO 8503-2 (G). The surface of thin-plate can be prepared e.g. by phosphating. OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities that might be detrimental to the application of paint (e.g. grease and salts) are removed. The surfaces must be dry and clean. Old, painted surfaces that have exceeded the maximum overcoating time are to be roughened as well. Damaged parts are prepared in accordance with the requirements of the substrate and the maintenance coating. ZINC SURFACES: Hot-dip-galvanized steel structures that are exposed to atmospheric corrosion can be painted if the surfaces are sweep blast-cleaned (SaS) till matt all over. Suitable cleaning agents are, e.g. aluminium oxide and natural sand. It is not recommended according to standard ISO 12944-5 to paint hot-dip-galvanized objects that are subjected to immersion strain. Painting of hot-dip-galvanized objects that are subjected to immersion strain must be discussed separately with Teknos. ALUMINIUM SURFACES: Treat the surfaces with suitable Cleaning Agent. Surfaces that are exposed to weathering are also roughened up with sweep blast-cleaning (AlSaS) or sanding. The place and time of the preparation are to be chosen so that the prepared surface will not get dirty or damp before the subsequent treatment. Additional instructive information for surface preparation can be found in standards EN ISO 12944-4 and ISO 8501-2.

MIXING OF THE COMPONENTS: Take into consideration the pot life of the mixture when estimating the amount to be mixed at a time. The base must be stirred until it is homogeneous before mixing the components. Before application the base and hardener are mixed in right proportion. Stir thoroughly down to the bottom of the vessel. The stirring time is at least 5 min. Inadequate stirring or incorrect mixing ratio results in imperfect curing and impaired film properties.

The surface to be treated must be dry and the relative air humidity below 80%. During the application and drying period the temperature of the ambient air and the surface shall be at least above +5°C, and the temperature of the product above +15°C during mixing and spraying. Additionally, the temperature of the surface to be treated and the product must be at least +3°C above the dew point of the ambient air.

The ready paint reacts with air humidity. Use opened paint (base (comp. A)) within two weeks. Store in a cool place and in tightly closed containers. The storage stability is limited.

Suitable airless nozzle size 0.013 - 0.017" Suitable conventional spray nozzle size 1.8-2.2 mm, pressure 3 bar. All equipment that will be in direct contact with the paint must be cleaned before use with a thinner suitable for the paint.