TEKNODUR 0130
Polyurethane top coat
- UV resistant
- Wear resistant
- 2-component
- Topcoat
TEKNODUR 0130 is a two-pack polyurethane top coat. The hardener is an aliphatic isocyanate resin.
TEKNODUR 0130 is used as a top coat on steel and metal, e.g. for textured painting. The paint produces a semi-matt, UV-resistant film with good mechanical and weather resistance. If required, the application will give a textured pattern.
Technical data sheet
Surface preparation
Remove from the surfaces any contaminants that might be detrimental to surface preparation and application. Remove also water-soluble salts by using appropriate methods. The surfaces are prepared according to the different materials as follows:
OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities that might be detrimental to the application of paint (e.g. grease and salts) are removed. The surfaces must be dry and clean. Old, painted surfaces that have exceeded the maximum overcoating time are to be roughened as well. Damaged parts are prepared in accordance with the requirements of the substrate and the maintenance coating.
The place and time of the preparation are to be chosen so that the prepared surface will not get dirty or damp before the subsequent treatment.
Additional instructive information for surface preparation can be found in standards EN ISO 12944-4 and ISO 8501-2.
Application
MIXING OF THE COMPONENTS: Take into consideration the pot life of the mixture when estimating the amount to be mixed at a time. Before application the base and hardener are mixed in right proportion. Stir thoroughly down to the bottom of the vessel. Inadequate stirring or incorrect mixing ratio results in imperfect curing and impaired film properties.
Stir thoroughly before use.
Apply by conventional spray or airless spray. Suitable airless nozzle size 0.011 - 0.013".
To obtain a TEXTURED FINISH use conventional spray. Spray two normal coats and allow to dry for at least 15 min. Lower the spraying pressure considerably (to about 1 kp/cm²) and spray one additional coat so that the mist falls in drops. This gives a rough, textured surface that does not level before it dries.
Application conditions
The surface to be treated must be dry. During the application and drying period the temperature of the ambient air, the surface and the product shall be above +5°C and the relative air humidity below 80%. Additionally, the temperature of the surface to be treated and the product must be at least +3°C above the dew point of the ambient air.
Storage
The storage stability is shown on the label. Store indoors in a cool and dry place and in a tightly closed can.
The hardener reacts with air humidity and therefore the opened can is to be kept carefully closed, and it is recommended to be used within 14 d of opening.
| Total mass of solids | abt. 890 g/l |
|---|---|
| Volatile organic compound (VOC) | abt. 430 g/l |
| Pot life | 6 h (+23 °C) |
| Mixing ratio | 4:1 by volume (comp. A : comp. B) |
| Hardener | Comp. B: TEKNODUR HARDENER 0100/0200 |
| Gloss | Semi-matt |
| Tinting system | Teknomix;Teknotint |
| Practical spreading rate | The values depend on the application technique, surface conditions, overspray, etc. |
| Drying time – dust free | 1 h (ISO 9117-3:2010) |
| Drying time – touch dry | 6 h (ISO 9117-5:2012) |
| Thinner | Standard thinners: TEKNOSOLV 9526 and TEKNOSOLV 6220. Other thinners suitable for the product: see Thinning. |
| Clean up | TEKNOCLEAN 6496. Before use clean the spray gun and mixing vessels with a thinner suitable for the paint. |
| Colours | Same tinting system should be used during the whole painting project. Factory colours by agreement. |
| Safety markings | See safety data sheet. The hardener of the product and the ready mixture contain isocyanates. In poorly ventilated areas and especially when using spray application we recommend the use of a fresh air mask. In short or temporary work, a mask with combined filter A2-P2 can be used. In this case eyes and face are to be protected. The hardener can must be opened with caution, as pressure may develop in the can during storage. |