INFRALIT PE 8640-50
Low temperature curing polyester powder
- Low-temperature curing
- Powder coating
- Low-temperature curing
- Powder coating
INFRALIT PE 8640-50 is a TGIC-free powder coating based on solid high quality polyester resin. At elevated temperature the powder will melt, cure and form the final paint film.
INFRALIT PE 8640-50 is suitable for steel and aluminium constructions in objects where good weather resistance is required. INFRALIT PE 8640-50 forms a mechanically and chemically resistant paint film which has good corrosion resistance and good colour stability and gloss retention also in outdoor conditions. The powder coating is cured at a lower temperature than usual, as a result of which some of the reaction by-products do not evaporate from the surface of the paint film as they do at a higher temperature. This may appear in thicker parts of the material as pale ingredient or, in some cases, over the entire object. The phenomenon may cause a decrease in gloss, but the light mist can be wiped off with a soft cloth. At a metal temperature of at least 160°C for at least 10 minutes, the phenomenon will not occur. Low temperature curing powder coatings cure very fast. When optimizing the process, the curing must be assessed by various tests on the paint film and, if necessary, by measuring and evaluating the heating curves of the ovens.
Technical data sheet
Safety data sheet
Surface preparation
Storage
| Practical spreading rate | 6 - 10 m²/kg depending on the film thickness. |
|---|---|
| Spraying | CORONA |
| Curing time | 20 min/145°C (metal temperature) |
| Colours | By agreement. |
| Packages | 15 kg or 20 kg according to the density of the powder. |
| Safety markings | See safety data sheet. The powder itself is non-flammable, but with air it can form an explosive mixture that in presence of adequate ignition energy ignites. The lower explosion limit of typical powder coatings is between 20 g/m³ and 80 g/m³ (CEPE, Safe Powder Coating Guideline 8th Edition, 2020). Ventilation of the spray booth should be adjusted so that the concentration of powder in the air is less than 50% of the lower explosive limit value. On calculation of the powder concentration in the spray booth, the powder deposited on the workpiece is not taken into account. In order to avoid the discharge of powder from the booth into adjacent working spaces, the speed of air flow in the apertures of the booth must not fall below 0.5 m/s. Spray painters should wear dust masks and protective gloves. Any spatter of powder on the skin should be washed off with water and soap. |
| Gloss value | 65-99 |