EPINOX BOSMAN 77

Epoxy primer

  • Corrosion protective
  • Anti-osmose
  • Water resistant
  • 2-component
  • Primer
  • Solvent-borne

MIO pigmented, thixotropic, high solid, two components, epoxy primer, cured at low temperatures (down to -10ºC).

For renovation of boats from the laminate in order to prevent the phenomenon of osmosis. The hull corrosion protection of steel and aluminum yachts. For independent film of the inside surfaces of tanks (eg, bilge). As an intermediate in paint systems epoxy or epoxy-polyurethane.

Technical data sheet

Surface preparation

The degree of surface preparation depends on the type and operating conditions. Fill cavities in the substrate using epoxy putty first BOSMAN Wash the surface with water containing OLIVA CLEANER - should be dry, devoid of fat salt and dust. Steel and aluminium substrate should be primed with the paint ALU-STEEL PRIMER 2002 and wood – thinned WOOD PRIMER 12 .The surface of the laminate should be roughened with sandpaper does not exceed 1/3 of the gel coat.

Application

Airless spray, brush. When using a brush it may be necessary to apply several layers to achieve recommended coating thickness. Airless spray parameter - nozzle size: 0,48 - 0,63 mm, nozzle pressure: 20 - 25 MPa.

Application conditions

Minimum surface temperature: -5°C (surface frost- and ice-free) and at least 3°C higher than dew point, minimum temperature of paint itself +15ºC, ambient temperature not lower than -10oC, relative air humidity below 95%,good ventilation.
Solids abt. 65 % by volume
Volatile organic compound (VOC) abt. 300 g/l
Pot life 3,5 h (+23 °C)
Mixing ratio 100:20 by volume (comp. A : comp. B)
Hardener Comp. B: UTWARDZACZ 177
Recommended film thickness Dry film (µm) 100. Wet film (µm) 160.
Drying time – dust free after 2 h
Drying time – touch dry after 8 h
Thinner Not recommended. When necessary (for example – thickening product) use TEKNOSOLV 564.
Clean up TEKNOSOLV 564
Packages Base: 0,6 l Hardener: 0,12 l
Safety markings See Safety Data Sheet