TEKNODUR ANTISLIP 9204-01

Polyurethan top coat

  • 2-component
  • Single coat paint
  • Solvent-borne
  • Top coat

TEKNODUR ANTISLIP 9204-01 is a two pack polyurethane paint with an aliphatic isocyanate as a hardener and slip-resistant properties.

The paint can be used as a topcoat in polyurethane coating systems in combination with a primer. With an appropriate surface preparation (SA2½, FePho, ZnPho) it can also be used as one layer coating system.

Low solvent content. Quick drying. Good mechanical and weather resistance. Excellent adhesion on different types of substrate. Structured surface which causes slip-resistant properties.

Surface preparation

Remove from the surface any contaminants that might be detrimental to surface preparation and coating. Remove also water-soluable salts by using appropriate methods. The surface should be prepared as follows: STEEL SURFACES: Remove mill scale and rust by blast cleaning to preparation grade Sa 2½ (standard ISO 8501-1). Roughening the surface of thin-plate improves the adhesion of the paint to the substrate. ZINC SURFACES: Hot-dip-galvanized steel structures that are exposed to atmospheric corrosion can be painted if the surfaces are sweep blast-cleaned (SaS) till matt all over. Suitable cleaning agents are, e.g. aluminium oxide and natural sand. It is not recommended to paint galvanized objects that are subjected to immersion strain. It is recommended that new zinc-coated thin-plate structures are treated with sweep blast-cleaning (SaS). Surfaces that have been weathered to matt can be treated also with PELTIPESU Cleaning Agent. The place and the time of the preparation are to be chosen so that the prepared surface will not get dirty or damp before subsequent treatment. OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities that might be detrimental to the application of paint (e.g. grease and salts) are to be removed. The surface must be dry and clean. Old, painted surfaces that have exceeded the maximum overcoating time are to be roughend as well. Damaged parts are prepared in accordance with the requirements of the substrate and the maintenance coating.
Solids abt. 66 % by volume
Volatile organic compound (VOC) abt. 310 g/l
Pot life 4 h (+23 °C)
Mixing ratio 9:1 by volume (comp. A : comp. B)
Hardener Comp. B: TEKNODUR HARDENER 7235 or TEKNODUR HARDENER 7500
Tinting system Teknotint
Recommended film thickness The recommended maximal film thickness is 80 µm dry film.
Drying time – dust free after 20 min
Drying time – touch dry after 1,5 h
Drying time – forced drying 60°C / 1 h (grasp)
Thinner TEKNOSOLV 6740
Clean up TEKNOSOLV 6740