TEKNODUR MIOX 3413 INACTIVE
Polyurethan top coat

- Corrosion protective
- 2-component
- Solvent-borne
- Top coat
Two-pack iron mica-containing polyurethane topcoat for robust and decorative corrosion protection.
High-quality, color-stable top coat for steel constructions.
Highly resistant against weathering and optimized colour stability. Good flexibility and mechanical resistance.
Technical data sheet
Surface preparation
Remove from the surface any contaminants that might be detrimental to surface
preparation and coating. Remove also water-soluble salts by using appropriate
methods. The surface should be prepared as follows:
Suitable primers are for e.g. TEKNOPOX PRIMER 3226 for blasted steel, as well
as TEKNOPOX PRIMER MIOX 3227 for hot dipped galvanized steel.
OLD PAINTED SURFACES SUITABLE FOR OVERCOATING: Any impurities
that might be detrimental to the application of paint (e.g. grease and salts) are to
be removed. The surface must be dry and clean. Old, painted surfaces that have
exceeded the maximum overcoating time are to be roughened as well. Damaged
parts are prepared in accordance with the requirements of the substrate and the
maintenance coating.
The place and time of the preparation are to be chosen so that the prepared
surface will not get dirty or damp before the subsequent treatment.
Solids | abt. 63 % by volume |
---|---|
Weight solids | abt. 79 % by weight |
Volatile organic compound (VOC) | abt. 330 g/l |
Pot life | 6 h (+23 °C) |
Mixing ratio | 6:1 by volume (comp. A : comp. B) |
Hardener | Comp. B: TEKNODUR HARDENER 7343 INACTIVE |
Gloss | Semigloss |
Recommended film thickness | The recommended maximal film thickness is 120 µm dry film. |
Drying time – dust free | 60 min |
Drying time – touch dry | after 9 h |
Drying time – through-dry | 12-16 h |
Drying time - overcoatable | after 12-16 h |
Thinner | TEKNOSOLV 6740 |
Clean up | TEKNOSOLV 6740 |