Other paint systems
Paint systems for surfaces subjected to high temperatures
EN ISO 12944-5 (2007) corrosivity category C4, durability range M
The coating system structure: ESIZn(R)70/1-SI60/1 FeSa 2 ½
EN ISO 12944-5 (2007) corrosivity category C4, durability range H
The coating system structure: SIZn(R)70/1-SI70/1 FeSa 2 ½
| Paint | P242a | P242b |
| TEKNOZINC SS 1K Zinc Silicate paint | 70 µm | - |
| INFRALIT SI 8009-05 Zinc silicone Powder | - | 70 µm |
| INFRALIT SI 8009-02 Silicone Powder | 60 µm | 70 µm |
| Total dry film thickness | 130 μm | 140 μm |
| Paint system VOC*, g/m² |
53 | 0 |
Camouflage paint systems
CHEMICALLY PREPARED SURFACES:
Marking of the system: Nm30-PE180/2-PNS
The coating system structure: PE180/2-Fe/Al/Zn
| Paint | Binder | K122a |
| INFRALIT PE 8317-10 AN100 | PE | 80 μm |
| INFRALIT PE 8431-10 N11/AN22/AN33/AN44 |
PE | 100 μm |
| Total dry film thickness | 180 μm | |
| Paint system VOC*, g/m² |
0 | |
| Pattern application over powder coating |
||
| INERTA 70 CAMOUFLAGE PAINT AN11/AN22/AN33/AN44 | 40 μm | |
| Total film thickness | 220 μm | |
| Paint system VOC, g/m² | 50 | |
MECHANICALLY CLEANSED SURFACES:
Paint system code K122b
Marking of the system: Nm30-PE180/2-PNS
The coating system structure: PE180/2-FeSa 2½
Marking of the system: Nm30-PE180/2-PNS
The coating system structure: PE180/2-AlSaS/ZnSaS
| Paint | Binder | K122b | K122c |
| INFRALIT PE 8316-05 | Zinc PE | 80 μm | - |
| INFRALIT PE 8317-10 AN100 |
PE | - | 80 μm |
| INFRALIT PE 8431-10 AN11/AN22/AN33/AN44 | PE | 100 μm | 100 μm |
| Total dry film thickness | 180 μm | 180 μm | |
| Paint system VOC*, g/m² |
0 | 0 | |
| Pattern application over powder coating | |||
| INERTA 70 CAMOUFLAGE PAINT AN11/AN22/AN33/AN44 | PUR | 40 μm | 40 μm |
| Total film thickness | 220 μm | 220 μm | |
| Paint system VOC, g/m² | 50 | 50 | |
*Teknos powder coating products are solvent-free. However, they might contain some volatile organic compounds as residuals from additives, though the quantities are very low.