2. EPINOX BOSMAN 54

EPINOX BOSMAN 54

Epoxy primer

»
  • Corrosion protective
  • Water resistant
  • 2-component
  • Solvent-borne
  • Primer

Two-component polyaminoamide cured epoxy enamel.

For the renovation of yachts from the laminate to prevent the phenomenon of osmosis. As an intermediate coating in the systems of epoxy or epoxy-polyurethane

The coating with high gloss, flexible and mechanically resistant, also with very good adhesion to the substrate. The coating is resistant to water, salt- and alkali- solutions, crude oil, vegetable oil, diesel oil and some aliphatic hydrocarbons. It is also resistant to spillages and splashes of diluted inorganic acids and aromatic hydrocarbons. Under the influence of the sun radiation, tint of the coating may change.

Surface preparation

The degree of surface preparation depends on the type and operating conditions. Fill cavities in the substrate using epoxy putty first BOSMAN Wash the surface with water containing OLIVA CLEANER - should be dry, devoid of fat salt and dust. Steel and aluminium substrate should be primed with the paint ALU-STEEL PRIMER 2002 and wood – thinned WOOD PRIMER 12 .The surface of the laminate should be roughened with sandpaper does not exceed 1/3 of the gel coat.

Application

Airless spray, brush. Airless spray parameter - nozzle size: 0,38 - 0,48 mm, nozzle pressure: 10 - 15 MPa.

Application conditions

Minimum surface temperature: +5°C and at least 3°C higher than dew point, relative air humidity below 85%, good ventilation.
Solids abt. 53 % by volume
Volatile organic compound (VOC) abt. 450 g/l
Pot life 10 h (+23 °C)
Mixing ratio 100:40 by volume (comp. A : comp. B)
Hardener Comp. B: UTWARDZACZ 197
Drying time – dust free after 1,5 h
Drying time – touch dry after 7 h
Thinner Not recommended. When necessary (for example – thickening product) use TEKNOSOLV 9506.
Clean up TEKNOSOLV 9506
Packages Base: 0,52 l Hardener: 0,21 l