EPIRUST ALU-STEEL PRIMER 2002
Epoxy primer
- Corrosion protective
- Water resistant
- 2-component
- Solvent-borne
- Primer
Two components, modified epoxy primer, fast curing with amine adduct.
Priming the hulls and equipment parts from steel, aluminum and cast iron.
Can be applied on wet and not well cleaned surfaces, humidity insensitive. The coating cures very fast even in low temperatures and is not sensitive to water (rain) when cured to touch dry degree.. High reactive coating with long pot life. Flexible coating, with good adhesion to surfaces and resistant to mechanical factors. The coating resistant to weathering, water, salt and alkali solutions, oil, fuel oil, diesel, motor gasoline and some organic solvents. Coating resistant to the elements occurring in the cathodic protection.
Technical data sheet
Surface preparation
It is recommended to wash surface with water with addition of OLIVA CLEANER and then rinse with fresh water.
Application
Airless spray, brush. When using a brush it may be necessary to apply several layers to achieve recommended coating thickness. Airless spray parameter - nozzle size: 0,38 - 0,48 mm, nozzle pressure: 15 – 20 MPa.
Application conditions
Minimum surface temperature: -5°C (surface frost- and ice-free), minimum temperature of paint itself +15°C, ambient temperature not lower than -10°C, relative air humidity below 95%, good ventilation.
| Solids | abt. 51 % by volume |
|---|---|
| Volatile organic compound (VOC) | abt. 380 g/l |
| Pot life | 6 h (+23 °C) |
| Mixing ratio | 100:22 by volume (comp. A : comp. B) |
| Hardener | Comp. B: UTWARDZACZ 161 |
| Drying time – dust free | after 15 min. |
| Drying time – touch dry | after 50 min. |
| Thinner | Not recommended. When necessary (for example – thickening product) use TEKNOSOLV 564. |
| Clean up | TEKNOSOLV 564 |
| Packages | Base: 0,6 l Hardener: 0,14 l |
| Safety markings | See Safety Data Sheet |